| LLMF-116D is a certified prime resin designed for production of Blown films needing excellent optics, superior film strength and excellent heat seal performance. LLMF-116D applications include heavy duty packaging, ice bags and sealant layer in coextrusions. LLMF-116D contains medium slip, high antiblock and process aid. LLMF-116D complies with FDA regulation 21CFR 177.1520(c)3.2a, conditions of use B-H. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.4 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 172 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 13.1 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 9.93 | MPa | ASTM D882 |
| MD : Break, 25 µm | 52.7 | MPa | ASTM D882 |
| TD : Break, 25 µm | 46.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 480 | % | ASTM D882 |
| TD : Break, 25 µm | 600 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 800 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 230 | g | ASTM D1922 |
| TD : 25 µm | 500 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 93 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film; blow-up-ratio 2.5 :1; Melt temperature 400°F |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210G15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Witcom PA6 2011/200 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| AKROMID® B3 GF 50 1 black (2488) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LEXAN™ 104R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Hifax CA 1168 A 3001 S1 | LyondellBasell Industries | PP Copolymer | Hifax |