Innothane® IE-70D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L4glKn_Innothane-IE-70D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-70D is a 70 shore D polyurethane formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.06 | g/cm³ | |
| Cured | 1.10 | g/cm³ | |
| Base Resin | 1.10 | g/cm³ | |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 52 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 360 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.045 | Pa·s | |
| 25°C 2 | 0.20 | Pa·s | |
| 25°C 3 | 0.80 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 14 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 36.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 4.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 30 FR0 HF NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Vyncolit® E 8398 | Vyncolit N.V. | Epoxy | Vyncolit® |
| Fainplast PVC HGKA 78 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina IVORY PVC COMPOUND 90900-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8205-85 Blue 8407 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |