Ghaed ABS ABS-65
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L4GhdX_Ghaed-ABS-ABS-65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General grade. Characteristic: General plating , poor solvent paint. Application: Electronic and Electrical parts, Automobile parts, Refrigerator knobs,Motorcycle parts, house appliances, Cosmetic case,etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 to 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 40.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 25 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1860 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 53.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 25 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 93.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 215 to 225 | °C | |
| Processing (Melt) Temp | 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 9813 | Colorite Polymers | PVC, Unspecified | Unichem |
| Ferro PP WPP10SD04BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Huaxia Shenzhou PVDF DS205 | Shandong Huaxia Shenzhou New Material Co., Ltd. | PVDF | Huaxia Shenzhou |
| OnFlex™ U 5470A-E0083 | PolyOne Corporation | TPE | OnFlex™ |
| LNP™ LUBRICOMP™ Noryl_NWR5810 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |