Symbios® 4102
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Braskem |
| Trademark: | Symbios® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3SOKW_Symbios-4102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Braskem Symbios 4102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on biorented films (BOPP), with heat seal temperature below 120°C on treated face. This product does not have slip and anti-blocking agents so its indicated for customized formularization. This product is appropriate for metallizing processes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 79 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus | 700 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm, Blown Film | 395 | MPa | |
| 1% Secant, TD : 30 µm, Blown Film | 395 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, Blown Film | 18.0 | MPa | |
| TD : Yield, 30 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 30 µm, Blown Film | 16 | % | |
| TD : Yield, 30 µm, Blown Film | 13 | % | |
| Seal Initiation Temperature (30 µm, Blown Film) | 99.0 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 20 | J/m | |
| 23°C | 50 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 48.0 | °C | |
| 1.8 MPa, Unannealed | 74.0 | °C | |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 96 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 0.40 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4275 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sanren Y2600T (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Versalloy™ HC 9210-45N | PolyOne Corporation | TPE | Versalloy™ |
| Fainplast PVC PM 5525 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Karina STRAW PVC COMPOUND 701-38/ 14-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |