GLS Nylon 6 PG69
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3R2Lw_GLS-Nylon-6-PG69.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon6 30% GF Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 to 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 135 to 145 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus 3 | 8000 to 8500 | MPa | ASTM D790 |
| Flexural Strength 4 | 215 to 225 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 to 95 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 245 to 280 | °C | |
| Mold Temperature | 55.0 to 95.0 | °C | |
| Injection Pressure | 68.0 to 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4702-715UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| TECHNO ABS F5452 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Ferro PP NPP00GC17NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Ecotan B FM SB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| INSTRUC PBTGF10 | Infinity LTL Engineered Compounds | PBT | INSTRUC |