TRIBOCOMP® PA66 CF30 TS0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L3GC4t_TRIBOCOMP-PA66-CF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PA66 CF30 TS0 is a polyamide 66 (nylon 66) product, which contains 15% ptfe fiber and 30% carbon fiber reinforced materials. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 22000 | 17000 | MPa | ISO 527-2 |
| 90°C | 15000 | -- | MPa | ISO 527-2 |
| 120°C | 11000 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Fracture, 23°C | 230 | 170 | MPa | ISO 527-2 |
| Fracture, 90°C | 135 | -- | MPa | ISO 527-2 |
| Fracture, 120°C | 120 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 20000 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 350 | 255 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| Dynamic | 0.14 | -- | ASTM D3702 | |
| Static | 0.12 | -- | ASTM D3702 | |
| Wear Factor | 9.00 | -- | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.51 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+2 | -- | ohms | ASTM D257 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 275 - 295 | °C | |
| Front Temperature | 280 - 295 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 - 130 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPA66 GF 30 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | Nylon 66 | RC Plastics |
| Royalite R24 | Spartech Plastics | ABS | Royalite |
| Unichem 5612 | Colorite Polymers | PVC, Unspecified | Unichem |
| ISOTHANE® 1680A-E | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| Hostacom TRC 787N | LyondellBasell Industries | TPO (POE) | Hostacom |