LNP™ THERMOCOMP™ DF0081PI compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L2i06w_LNP-THERMOCOMP-DF0081PI-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP DF0081PI is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, good flatness, Non-Brominated & Non-Chlorinated Flame Retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.40 | % | |
| Across Flow | 0.41 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12700 | MPa | ASTM D638 |
| -- | 12500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 130 | MPa | ASTM D638 |
| Break | 123 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.8 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 10000 | MPa | ASTM D790 |
| -- 5 | 10800 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 170 | MPa | ASTM D790 |
| Flexural Strain at Break 7 | 1.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 81 | J/m | ASTM D256 |
| 23°C 8 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D4812 |
| 23°C 9 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 102 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 285 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.100 to 0.300 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 1035FS20 | Reliance Industries Limited | LDPE | RELENE® |
| Mediprene® A2 500350M | ELASTO | SEBS | Mediprene® |
| Siloxane Masterbatch MB50-002 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Nypol® PA B3 HL CNZ0311 NT362 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Americas Styrenics MC9540 | Americas Styrenics LLC | PS (GPPS) | Americas Styrenics |