Geon™ HTX Ultra LA436G Black 2880
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L2ZONe_Geon-HTX-Ultra-LA436G-Black-2880.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon HTX Ultra LA426 has a higher gloss product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 441311640000 | ASTM D4216 | |
| PVC Cell Classification | 14215 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1920 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 36.0 | MPa | ASTM D638 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Flexural Strength | 58.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 490 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 52.0 | J/cm | ASTM D4226 |
| 23°C 4 | 111 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 88.3 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 87.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 81.1 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 85.0 | °C | ASTM D648 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 推荐在华氏160度下将材料干燥至少2小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 612 GF33 | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Sinvicomp SRF3707 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| SUMIKASUPER® LCP E6010 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Elastron® G G501.A35.N.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina CLEAR PVC COMPOUND 80/211-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |