Telcar® TL-1000-105UV
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L2VlI9_Telcar-TL-1000-105UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TL-1000-105UV is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 379 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 12.5 | MPa | ASTM D412 |
| Tensile Strength (Break) | 20.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 700 | % | ASTM D412 |
| Tear Strength 1 | 127 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 45 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.0 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1400 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Witcom PA66 2C | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Hapflex™ 668-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| LUVOCOM® 1850-7315 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Osterlene® LD02520A | Osterman & Company | LDPE | Osterlene® |