Synthos PS HI 552M
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L22IIO_Synthos-PS-HI-552M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SYNTHOS PS HI 552M is high-impact polystyrene (HIPS) with a balanced combination of rheological, mechanical and thermal properties, suitable for general application use. It is a thermoplastic material designed for injection moulding and extrusion. Product has a form of lens granules of diameter 2,5 to 4 mms. APPLICATION Injection moulding is used to produce consumer goods and technical components that are exposed to higher mechanical stress. Good results are achieved in extruded profiles. The composition of the polymer meets the requirements of the Health and can therefore be used for the production of articles coming into contact with food. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 9.0 to 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | Internal Method |
| Particle Size | 2.50 to 4.00 | mm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene | 0.025 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 120 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Desiccant Dryer | 80.0 | °C | |
| Hot Air Dryer | 70.0 | °C | |
| Drying Time | |||
| Desiccant Dryer | 1.0 | hr | |
| Hot Air Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 260 | °C | |
| Mold Temperature | 10.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1262B | Teknor Apex Company | TPE | Sarlink® TPE |
| DOW™ LLDPE DNDA-8320 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Cevian®-V 450SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| KumhoSunny PC/ABS HAC8265 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| OTECH PVC OW930 - A/V Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |