Next Nylon 6 Prime Series NM40-01BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L21Q6Q_Next-Nylon-6-Prime-Series-NM40-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Mineral Fillled Black compound Product Applications Generally recomended for application such as marine hardware, brackets, fitting, bobbins, and power tool housing Benefits High stiffness, dimensional stability including low warp and resistance to sink mark |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.49 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.65 | -- | % | ASTM D955 |
| Transverse flow | 0.65 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.5 | -- | % | ASTM D570 |
| Saturation 1 | 5.7 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 105 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6400 | 3800 | MPa | ASTM D638 |
| Tensile Strength | 85.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | 15 | % | ASTM D638 |
| Flexural Modulus | 5200 | -- | MPa | ASTM D790 |
| Flexural Strength | 140 | 70.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 190 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Mold Temperature | 80.0 - 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 1001 | Teknor Apex Company | PVC, Flexible | APEX® |
| CGPC PVC R-10X NI Extrusion | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| ECP 21150 | TBA Electro Conductive Products Ltd. | TPU-Polyether | ECP |
| IDI BMC Rosite 3550F | IDI Composites International | TS, Unspecified | IDI BMC |
| Paryls® PES F2250 GL30 | Youju New Materials Co., Ltd. | PESU | Paryls® |