Quadrant EPP Quicksilver® Premium Truck Lining
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L1esZR_Quadrant-EPP-Quicksilver-Premium-Truck-Lining.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Quicksilver® Premium Truck Lining is an Ultra High Molecular Weight Polyethylene product. It is available in North America. Typical application: Bags/Liners. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 483 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 30.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 230 | % | ASTM D638 |
| Flexural Modulus | 455 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 24.1 | MPa | ASTM D790 |
| Compressive Modulus | 552 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 20.7 | MPa | ASTM D695 |
| Shear Strength | 33.1 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.090 | Internal Method | |
| Abrasion 1 | 10 | ASTM D4020 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 2 | 0.0701 | MPa·m/s | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 135 | °C | ASTM D3418 |
| CLTE - Flow 3(-40 to 149°C) | 2.0E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Sand Slurry; 1018 Steel = 100 |
| 2 . | 4:1 safety factor |
| 3 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ GZ2540 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Trexprene® D50NU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| NEXT REPROCESSED POMC M270-300R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| Mafill® CF 4002/30 | Ravago Group | PP Copolymer | Mafill® |
| Domamid HT™ 7750R60H3 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |