Plexiglas® DRG-100
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L1CkuF_Plexiglas-DRG-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® DRG-100 is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. This grade is formulated for approved medical applications and has improved gamma resistance compared to DR-100G. It is a heat resistant resin with minimal edge color and provides 10 times the impact resistance of standard acrylics. It is an all-acrylic resin that combines the toughness associated with other impact plastics and the outstanding transparency and UV resistance of conventional acrylic materials. Moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 45 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 88.9 | °C | |
| 1.8 MPa, Annealed | 79.4 | °C | |
| Vicat Softening Temperature | |||
| -- | 97.8 | °C | ASTM D1525 2 |
| -- | 86.1 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 90.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 2.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0231V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 FR HS | RTP Company | Nylon 66 | RTP |
| Catalyst CT/7 UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| ENFLEX V1075A | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| Latilub 66-10T G/30-V0KB1 | LATI S.p.A. | Nylon 66 | Latilub |
| LNP™ STAT-KON™ DE003E compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |