Riblene® FC 40 F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L16Kde_Riblene-FC-40-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FC 40 F is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 40 F is characterised by a high melt strength leading to a good bubble stability during extrusion. Main Application Riblene FC 40 F is recommended for the production of shrink film for medium and high loads characterized by high rigidity, clarity and gloss. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 40 to 150 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 240 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 28.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 28.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 550 | % | |
| TD : Break, 70 µm, Blown Film | 650 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 290 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 35.0 | kN/m | |
| TD : 70.0 µm | 50.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ISO 306/A |
| Melting Temperature | 116 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 1 S3 natural (2847) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Capran® 1200M | Honeywell | Nylon 6 | Capran® |
| Karina MBU BLUEL -E 06/923-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina RED COLOR CONCENTRATE 42/154-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5132-75 Clear Yellow 4164 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |