DESLON™ 66 DSC221M8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KzT8U0_DESLON-66-DSC221M8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC221M8 is one of the brands which made by Polyamide66 that filled Mineral Filler 40% and reinforced goods. It provides high mechanical strength, good dimensions stability property. Applications: DESLON™ DSC221M8 is one of the most-used resin requested for high mechanical strength, good dimensions stability property goods, such as PB Pipe Cap and Mechanical, Automotive parts, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 83.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5880 | MPa | ASTM D790 |
| Flexural Strength | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 235 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 215 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 285 | °C | |
| Front Temperature | 285 - 290 | °C | |
| Nozzle Temperature | 280 - 285 | °C | |
| Processing (Melt) Temp | 280 - 285 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1012-FR | QTR, Inc. | PC | QR Resin |
| Royalite R722 | Spartech Plastics | PMMA+PVC | Royalite |
| DELPET™ 80NH | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Innova SR 550 | Innova SA | PS (HIPS) | Innova |
| Karina CLEAR PVC COMPOUND -E 70/200-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |