Tecnoprene® A60K4 NAT001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KyZ0oO_Tecnoprene-A60K4-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer reinforced with 20% chemically coupled glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Ash Content | 20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638 |
| Flexural Modulus | 4300 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 90 | J/m | |
| 23°C | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 145 | °C | ASTM D648 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 1 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.40 | ASTM D150 | |
| Comparative Tracking Index | 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (ABS/PA) M/MK SF | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| AKROMID® T1 ICF 20 black (5147) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| Idemitsu PS NS-300 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| Deprene 151-70 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| 3M™ Dyneon™ Fluoroelastomer FC 1610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |