Lumax® GN5006FC
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kxm0m1_Lumax-GN5006FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant Applications IT/OA, E&E |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 13 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 70.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 80.0 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 225 to 235 | °C | |
| Front Temperature | 225 to 235 | °C | |
| Nozzle Temperature | 230 to 245 | °C | |
| Processing (Melt) Temp | 230 to 245 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 215 to 235 | °C | |
| Cylinder Zone 2 Temp. | 225 to 245 | °C | |
| Cylinder Zone 3 Temp. | 225 to 245 | °C | |
| Cylinder Zone 4 Temp. | 225 to 245 | °C | |
| Adapter Temperature | 225 to 245 | °C | |
| Melt Temperature | 215 to 245 | °C | |
| Die Temperature | 215 to 235 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4110G33 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Baydur® 661 IBS (30 pcf, 20% Wollastocup) | Covestro - PUR | PUR-MDI | Baydur® |
| APEX® 3174 | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ LUBRICOMP™ RZL36 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| OTECH ALLOY NT1000-80 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |