TUFNYL® SGF 30 FR0 HF NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SRF Ltd. |
| Trademark: | TUFNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KxK5pl_TUFNYL-SGF-30-FR0-HF-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 30% Glass fiber reinforced, flame retardant, halogen free material for injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.35 | % | Internal Method |
| Water Absorption (Equilibrium) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 81 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 49.0 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index | > 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Shin-Etsu RTV KE-3421 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Chemical Resources PMMA600 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| Elastollan® L 785 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| ADVANCENE™ EM-5204-UVH | ETHYDCO | HDPE | ADVANCENE™ |