LNP™ THERMOCOMP™ RB008 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kw9bTB_LNPTHERMOCOMPRB008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing Glass Bead. Also known as: LNP* THERMOCOMP* Compound RB-1008 Product reorder name: RB008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.8 - 2.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 - 2.1 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 - 2.1 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.8 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 1.2 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5100 | MPa | ASTM D638 |
| -- | 5440 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 55.3 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.3 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3780 | MPa | ASTM D790 |
| -- | 4060 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 2.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D4812 |
| 23°C 3 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.77 | J | ASTM D3763 |
| -- | 4.85 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 68.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 102 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP500V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Generic Nylon 6I/6T - Glass Fiber | Generic | Nylon 6I/6T | Generic |
| KOCETAL® GF305LO | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Mafill® CR C 4044 | Ravago Group | PP Copolymer | Mafill® |
| Polygen SC73C-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |