Devcon Stainless Steel Putty (ST)
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kvw8up_Devcon-Stainless-Steel-Putty-ST-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A stainless steel-filled epoxy for rebuilding and repairing stainless steel equipment. Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.50 | g/cm³ | |
| Specific Volume | 0.448 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 121 | °C | |
| Wet | 49 | °C | |
| Tensile Shear Adhesion | 16.4 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Flexural Strength | 36.4 | MPa | ASTM D790 |
| Compressive Strength | 57.9 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.51 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 1.2 | kV/mm | ASTM D149 |
| Dielectric Constant | 75.0 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 11 Mixing ratio by capacity: 3.8 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 58 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT750 | Sasol Polymers | LDPE | Sasol Polymers PE |
| HK HIPS PDR751 | Hong Kong Petrochemical Co. Ltd. | PS (HIPS) | HK HIPS |
| LG PS 20HR(E) | LG Chem Ltd. | PS (HIPS) | LG PS |
| PETILEN I 768(UV) | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |
| Osterlene® LLH1018A | Osterman & Company | LLDPE | Osterlene® |