GLS 287-094 Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
GLS 287-094 is a custom, precolor grey TPE compound

General Information
Features	Workability, good Good adhesion Excellent appearance
Appearance	Grey
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.11	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	59		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (300% Strain, 23°C)	2.55	MPa	ASTM D412
Tensile Strength (Break, 23°C)	2.55	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	370	%	ASTM D412

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	20.0	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Suggested Max Regrind	20	%
Rear Temperature	166 - 193	°C
Middle Temperature	249 - 260	°C
Front Temperature	254 - 277	°C
Nozzle Temperature	254 - 277	°C
Processing (Melt) Temp	260 - 277	°C
Mold Temperature	16 - 38	°C
Back Pressure	0.00 - 0.689	MPa
Screw Speed	75 - 175	rpm

Injection instructions
Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polpropylene (PP).Regrind levels up to 20% can be used with GLS 287-094 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.GLS 287-094 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 2.5 to 5 in/sec1st Stage - Boost Pressure: 400 to 600 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 3 to 6 secHold Time (Thin Part): 1 to 3 sec

Injection instructions

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polpropylene (PP).Regrind levels up to 20% can be used with GLS 287-094 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.GLS 287-094 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 2.5 to 5 in/sec1st Stage - Boost Pressure: 400 to 600 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 3 to 6 secHold Time (Thin Part): 1 to 3 sec

Resin Grade	Manufacturer	Category	Trademark
Starflam PK0049	Eurostar Engineering Plastics	Nylon 6	Starflam
DynaMix™ 2044-SGB	Polymer Dynamix	Nylon, Unspecified	DynaMix™
GLS Nylon 6 PG69	GLS Polymers Pvt. Ltd.	Nylon 6	GLS Nylon 6
Keysor PVC KYNS	Keysor-Century Corporation	PVC, Unspecified	Keysor PVC
Sylvin 8205-75UV Brown 7448	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	GLS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KvigL6_GLS287094.pdf
PRICE:	Order Products email sales@su-jiao.com