Bapolene® 222F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KuOqyf_Bapolene-222F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LL222F is a general purpose LLDPE for blown film extrusion or cast film applications. This resin offers excellent tensile and toughness properties. It is available with and without slip/antiblock additives. This product meets FDA standards for food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus 1 | ASTM D882 | ||
| MD : 38 µm, blown film | 200 | MPa | ASTM D882 |
| TD : 38 µm, blown film | 241 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.00 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 9.80 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 26.9 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 20.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 800 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 250 | g | ASTM D1922 |
| TD : 38 µm, blown film | 620 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (37.5 µm, blown film) | 38 | ASTM D2457 | |
| Haze (37.5 µm, blown film) | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties are based on a thickness of 37.5 µm and blow-up ratio of 2:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 227 | °C |
| Note Message | |
|---|---|
| 1 . | 0.10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ333G2 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Unichem 9500UVF | Colorite Polymers | PVC, Unspecified | Unichem |
| KRATON® G4609 H | Kraton Polymers LLC | SEBS | KRATON® |
| Huafon JF-W-AH6065 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina RED COLOR CONCENTRATE 42/165-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |