RELENE® 52GF004
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KuCYCz_RELENE-52GF004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 52GF004 is a blown film grade of High Molecular Weight High Density Polyethylene (HMHDPE). It possesses broad molecular weight distribution, which improves processability. 52GF004 can readily be processed on HMHDPE blown film extrusion lines. The films will have homogeneous, finely textured, opaque appearance and exhibit balanced mechanical properties and very good gloss. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.45 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 20 µm | 30.0 | MPa | |
| TD : Yield, 20 µm | 32.0 | MPa | |
| MD : Break, 20 µm | 50.0 | MPa | |
| TD : Break, 20 µm | 48.0 | MPa | |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 20 µm | > 600 | % | |
| TD : Break, 20 µm | > 600 | % | |
| Dart Drop Impact 3 | 6.0 | g | ASTM D1709 |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 20 µm | 0.60 | g | |
| TD : 20 µm | 9.2 | g |
| Note Message | |
|---|---|
| 1 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| 2 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| 3 . | F50, 38mm dart, 66cm height |
| 4 . | 20 µm film made with 0.75mm die gap & 4 BUR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PE CC0551BK | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| TOTAL Polyethylene HDPE 2285 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| DENKA POVAL F-300S | Denka Company Limited | PVOH | DENKA POVAL |
| Fluon® PTFE PB3060 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| SEQUEL® 1514UV LF 11BK | LyondellBasell Industries | TPO (POE) | SEQUEL® |