EVAL™ LT171B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KtVrQo_EVAL-LT171B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
27 mol% Ethylene Vinyl Alcohol Copolymer LT171B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Ethylene Content | 27.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 13 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 2.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 4.3E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.026 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 1.9 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Melting Temperature | 191 | °C | ISO 11357 |
| Peak Crystallization Temperature | 164 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P256-762 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SCANTEC PC S90R | Polykemi AB | PC | SCANTEC |
| NatureFlex™ 110NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| LNP™ STAT-KON™ RE0039 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Sylvin 7833-85 Blue 8431 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |