Ferro PP TPP40AC50HB-BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kt2N0E_Ferro-PP-TPP40AC50HB-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP40AC50HB-BK is a Polypropylene material filled with 40% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 53.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Gardner Impact | 1.13 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 132 | °C | |
| 1.8 MPa, Unannealed | 76.7 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 210 | °C | |
| Middle Temperature | 210 to 213 | °C | |
| Front Temperature | 213 to 216 | °C | |
| Nozzle Temperature | 216 to 218 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer F70C | Precision Polymer Engineering Ltd. | Fluoro Si | Precision Polymer |
| Ravago Compounds HM-269H-1000 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| Sylvin 5186-85 White 1451 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Celanex® 3209HR | Celanese Corporation | PBT | Celanex® |
| CERTENE™ MWG-1238 | Muehlstein | MDPE | CERTENE™ |