Wechat:
| Message |
|---|
|
LNP STAT-KON EX99689C is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-E-99689 CCS Product reorder name: EX99689C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.36 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.30 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11700 | MPa | ASTM D638 |
| -- | 12600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 161 | MPa | ASTM D638 |
| Break | 137 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.6 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 50.0 mm Span 2 | 8000 | MPa | ASTM D790 |
| -- 3 | 7700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 242 | MPa | ASTM D790 |
| -- | 216 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 4 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 5 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 2.41 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 206 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 207 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.350 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 MG 30 | RTP Company | Nylon 66 | RTP |
| APEX® 85-J438D-6 | Teknor Apex Company | PVC, Flexible | APEX® |
| DURACON® AW-09 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| PURGOVIN® 3000 | Axiall Corporation | PVC, Unspecified | PURGOVIN® |
| Kinta FR6000 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |