PENTAMID AB S GVB16 H black
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ks2sQz_PENTAMIDABSGVB16Hblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, heat stabilised polyamide 66+6, glass fiber and glass bubbles reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.85 | % | ISO 294-4 |
| Flow | 0.50 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 7.1 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | % | ISO 62 |
| Viscosity Number | 125 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66 + 6, MHRC, 12-060, ( GF+ GB ) 16, X | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.030 - 0.11 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 285 - 310 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 90.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN0720SB | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| RELENE® M60075 | Reliance Industries Limited | HDPE | RELENE® |
| TOTAL Polystyrene Compound 9217 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| COSMOPLENE® FC9414G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| POLIFAIN 6020 | Fainplast Compounds S.r.l | PVC, Unspecified | POLIFAIN |