FERREX® GPP30CC39HB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kniqr6_FERREX-GPP30CC39HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX®GPP30CC39HB is a polypropylene homopolymer (PP Homopoly) material, and its filler is 30% calcium carbonate filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. FERREX®The main features of the GPP30CC39HB are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2180 | MPa | ASTM D790 |
| Tangent : 23°C | 2520 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D256 |
| Dart Drop Impact | 16.7 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.6 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 31% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON™ 685D | Trinseo | PS (GPPS) | STYRON™ |
| Kingfa FRABS-V0 | Kingfa | ABS | Kingfa |
| LNP™ THERMOCOMP™ RF008XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| OmniLon™ PA6/6 U GR33 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| OLEFISTA™ QX0238B | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |