| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KmUq7N_SURPASSFPs116CX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SURPASS®FPs116-CX is a linear low density polyethylene material,. This product is available in North America and is processed by film extrusion or co-extrusion. SURPASS®The main features of the FPs116-CX are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 139 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 162 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 9.00 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 47.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 480 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 610 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 710 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 260 | g | ASTM D1922 |
| TD : 25 µm, blown film | 490 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 37 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 1(25.0 µm) | 690 | J/cm | Internal method |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MV SHI | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Ultramid® T KR 4340 G6 | BASF Corporation | Nylon 6/6T | Ultramid® |
| Ferro PP TPP40AJ30BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hifax DRS715X | LyondellBasell Industries | TPO (POE) | Hifax |
| Jampilen RC1601 | Jam Polypropylene Company | PP Random Copolymer | Jampilen |