LubriOne™ PC-000/5T-2S BK002
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KmCOCC_LubriOne-PC-000-5T-2S-BK002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE/Silicone lubricated polycarbonate compound |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2200 | MPa | ASTM D790 |
| Flexural Strength 3 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Mold Temperature | 90.0 - 110 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO R110MP | Prime Polymer Co., Ltd. | PP Impact Copolymer | PRIME TPO |
| Sinpolene MBB206 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Fainplast PVC KL 94 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| KOCETAL® WR101 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Lucky Enpla LGF1150 | Lucky Enpla Co LTD | PC | Lucky Enpla |