Order Products : sales@su-jiao.com
Chemiton CEJ7NA 40
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Franplast S.r.l. |
| Trademark: | Chemiton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Km46lv_Chemiton-CEJ7NA-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEBS based compound with good recovery and excellent machinability. Ideal for the production of gaskets of any kind. Application:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 90 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 40 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 3.00 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 750 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 15 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -30 to 90 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 0.0 | hr | |
| Rear Temperature | 170 to 200 | °C | |
| Middle Temperature | 175 to 205 | °C | |
| Front Temperature | 180 to 210 | °C | |
| Nozzle Temperature | 185 to 215 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SMOKEGUARD™ III 1021 NATURAL UV-FG | AlphaGary | PVC, Unspecified | SMOKEGUARD™ III |
| APEX® 87-L517B2 NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Arnitel® XG5855 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Chemlon® 235G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| DIGITALWAX® DC 300 | DWS Systems | Unspecified | DIGITALWAX® |