VALOX™ V4760 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kks5ko_VALOX-V4760-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% glass fiber reinforced, thin wall brominated FR, high flow, high CTI |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.30 | % | |
| Across Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10500 | MPa | ASTM D638 |
| -- | 10700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 125 | MPa | ASTM D638 |
| Yield | 126 | MPa | ISO 527-2/5 |
| Break 3 | 125 | MPa | ASTM D638 |
| Break | 126 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.2 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 2.2 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9500 | MPa | ASTM D790 |
| -- 7 | 9500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 190 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 188 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 77 | J/m | ASTM D256 |
| 23°C | 76 | J/m | ASTM D256 |
| -30°C 9 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 11 | 38 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 209 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 207 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 202 | °C | ISO 306/B50, ASTM D1525 13 |
| CLTE | |||
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 80°C | 1.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : 23 to 80°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.6E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.280 mm | V-0 | ||
| 1.50 mm | 5VA | ||
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 725 | °C | |
| 1.00 mm | 700 | °C | |
| 2.00 mm | 725 | °C | |
| 3.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Processing (Melt) Temp | 254 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTek KM6080 | KMI Group Inc. | PBT | PrimoTek |
| Monprene® CP-18926 | Teknor Apex Company | TPE | Monprene® |
| Hostacom BB 1161 F M 2689 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina COKE PVC COMPOUND 830-21/9-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7833-80 Orange 547 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |