TAISOX 3220
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kkef1g_TAISOX-3220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 3220 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 3220 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 147 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 206 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 35.3 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 27.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 800 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 61 | g | ASTM D1922 |
| TD : 38 µm, blown film | 650 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 43 | ASTM D2457 | |
| Clarity | 67.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 22 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecolen® HP10 GR10 NL | Eurotec Engineering Plastics | PP Homopolymer | Tecolen® |
| SUNPRENE® FA90EB | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| EMERGE™ PC 8330 | Trinseo | PC | EMERGE™ |
| ESPOLEX 903 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Karina SMOKY CLEAR PVC COMPOUND 801-27/ 13-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |