DEXFLEX® 756-68E
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | DEXFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KgGBX8_DEXFLEX-756-68E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DEXFLEX 756-68E is a thermplastic olefinic elastomer (TPO) designed for use as an automotive airbag cover with requirements to deploy at temperatures between -40°C and +100°C. DEXFEX 1012E material is engineered for passenger-side and side airbag covers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 14.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 300 | % | ASTM D638 |
| Flexural Modulus - Tangent | 380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Note Message | |
|---|---|
| 1 . | Type IV, 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miraprene® QS1621 | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Gallonprene® GP210-4506 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Geon™ Vinyl Flexible A5DM0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LAMIGAMID® 320 | Schwartz Technical Plastic | Nylon 6 | LAMIGAMID® |
| Latilub 57-30GRTS G/20 | LATI S.p.A. | PPA | Latilub |