Polylink Polymer PBT-11030-GFFR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kg0Ogz_Polylink-Polymer-PBT-11030-GFFR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Filled PBT compounds are manufacturedbycom pounding PBT with specially treated choppedglass and modified with additives to make parts withhigh mechanical properties, heat resistance and fire resistance.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 - 1.70 | g/cm³ | Internal method |
| Moisture Content | < 800 | ppm | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 108 - 127 | MPa | ASTM D638 |
| Flexural Modulus | 8340 - 8630 | MPa | ASTM D790 |
| Flexural Strength | 167 - 181 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 - 74 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 215 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 230 | °C | |
| Cylinder Zone 4 Temp. | 240 | °C | |
| Cylinder Zone 5 Temp. | 245 | °C |
| Extrusion instructions |
|---|
| Zone 6 : 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smooth-Cast® ColorMatch® 326 | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| SureSpec HD55-30 | Genesis Polymers | HDPE | SureSpec |
| MORETEC™ 0218CM | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| KOPA® KN332G30V0BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ THERMOCOMP™ RF006XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |