Infino WP-1059
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KdcwRP_InfinoWP1059.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WP-1059 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 45 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 112 | ASTM D785 | |
| R scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 53.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2100 | MPa | ASTM D790 |
| -- 3 | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 74.0 | MPa | ASTM D790 |
| -- 5 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 470 | J/m | ASTM D256 |
| 23°C 7 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 115 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50 - 70 | °C | |
| Injection Pressure | 68.6 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4mm |
| 7 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7210U | Spartech Polycom | PC | Spartech |
| Xuchuan XCS-2585C | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Amilan® CM8000 | Toray Resin Company | Nylon Copolymer | Amilan® |
| DynaChar™ 3534 | Polymer Dynamix | Polyolefin, Unspecified | DynaChar™ |
| Hylon® N1015HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |