EcoLon® 2200-BK1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | EcoLon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kbs21A_EcoLon-2200-BK1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoLon® 2200-BK1 is a Polyamide 66 (Nylon 66) material filled with 40% glass\mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of EcoLon® 2200-BK1: Eco-Friendly/Green. Typical application of EcoLon® 2200-BK1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.80 to 1.2 | % | |
| Flow : 23°C | 0.30 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 282 to 304 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Nozzle Temperature | 266 to 293 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3U Q721 | BASF Corporation | Nylon 6 | Ultramid® |
| ELASTOSIL® R 770/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Rotuba CAB B930 (4% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| Sylvin 5132-75 Clear Red 6237 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8392-60D Natural | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |