Quadrant EPP Fluorosint® HPV
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KbOsBW_Quadrant-EPP-Fluorosint-HPV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mica-filled PTFE provides a unique blend of strength and dimensional stability along with an excellent wear enhancing additive technology. This product provides excellent wear and stability in addition to FDA compliance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.05 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Saturation | 0.43 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 52 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1240 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 8.96 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 17.2 | MPa | ASTM D790 |
| Compressive Modulus | 503 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 27.6 | MPa | ASTM D695 |
| Shear Strength | 17.2 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.15 | Internal Method | |
| Wear Factor | 44 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 260 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.657 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 327 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 9.7E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PGHS35-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Axiall PVC 16903 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Forprene® 6NM901A75 | SO.F.TER. SPA | TPV | Forprene® |
| Hostacom SP98F/94 | LyondellBasell Industries | TPO (POE) | Hostacom |
| Karina ICE COLOR PVC COMPOUND -E 798-P-28/ 37-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |