HONES® PA66 G30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZfAz0_HONES-PA66-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Technology characteristics: 30% Glass fiber reinforced, heat-resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 150 | MPa | ASTM D638 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 75 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 265 | °C | |
| Middle Temperature | 220 to 265 | °C | |
| Front Temperature | 220 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNTIANHUA® CM90 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| LNP™ LUBRICOMP™ GL003XXP compound | SABIC Innovative Plastics Europe | PSU | LNP™ LUBRICOMP™ |
| Formolene® 6145O | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Sumikon® PM-TX115 | SBHPP | Phenolic | Sumikon® |
| LNP™ LUBRICOMP™ EX06405 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |