KOPLA PA66 KDG1040
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZeycz_KOPLA-PA66-KDG1040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDG1040 is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Asia Pacific. Primary attribute of KOPLA PA66 KDG1040: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 216 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 11800 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 299 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 257 | °C | |
| 1.8 MPa, Unannealed | 252 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Laprene® 830000968 | SO.F.TER. SPA | SEBS | Laprene® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| PermaStat® 205 | RTP Company | Nylon 66 | PermaStat® |
| Hostacom ERC 213N G62720 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ COLORCOMP™ 203RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |