Ultramid® BU50I BK-106
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KZPIV9_Ultramid-BU50I-BK-106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid Ultratough Nylon BU50I BK-106 is an unreinforced PA6, impact modified, pigmented black, injection molding product that maintains its impact strength and ductility to -40 deg F (-40 deg C). The extreme low temperature tolerance of Ultramid BU50I BK106 makes it ideal for applications in which the weldline impact strength at low temperatures is critical. Applications Ultramid BU50I BK-106 is generally recommended for automotive components, small engines, power tool parts and casings, cold weather and high impact sports gear, such as snowboards, ski components, helmets and hockey masks. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 | % | |
| Water Absorption | |||
| Saturation | 7.3 | % | ASTM D570 |
| Saturation, 23°C | 7.3 | % | ISO 62 |
| Equilibrium, 50% RH | 2.1 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 48.0 | MPa | ASTM D638 |
| Yield, 23°C | 44.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1790 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 67.0 | MPa | ASTM D790 |
| 23°C | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 GB 20 | RTP Company | PESU | RTP |
| Santoprene™ 291-60B150 | ExxonMobil Chemical | TPV | Santoprene™ |
| Telcar® TL-2519G | Teknor Apex Company | TPE | Telcar® |
| BP Flex D 6520 T BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| Fortron® 1140L4 | Celanese Corporation | PPS | Fortron® |