POPELEN QHCA-352M
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | POPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KYHYMC_POPELEN-QHCA-352M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Stiffness, High Impact Strength |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 4.4 | kJ/m² | |
| 23°C | 28 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 4.4 | kJ/m² | |
| 23°C | 28 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7F-7015U | Spartech Polycom | PC | Spartech |
| Unilex™ UP.700.935U | United Polychem | PE, Unspecified | Unilex™ |
| NEXT REPROCESSED PA6 8267-300R | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REPROCESSED |
| Niche PA6GF43N | Niche Polymer, LLC | Nylon 6 | Niche |
| Fainplast PVC PH 60/AS | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |