Derakane® 510B-400

Category:	Vinyl Ester , Vinyl Ester
Manufacturer:	Ashland Performance Materials
Trademark:	Derakane®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KWlAv6_Derakane-510B-400.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DERAKANE 510 B-400 Epoxy Vinyl Ester Resin is a low viscosity, unpromoted, flame retardant") epoxy vinyl ester. This resin offers offers exceptional processing characteristics including little to no foaming, excellent exotherm control, and industry-leading storage stability. Laminates made with DERAKANE 510 B-400 resin have achieved a flame spread of 25 (ASTM E-84). DERAKANE 510 B-400 resin gives final products with:

Excellent flame retardancy

High strength characteristics

Excellent impact strength and toughness

Fast wet-out and low drainage

Excellent corrosion resistance to acidic and alkaline environments

APPLICATIONS AND USE
DERAKANE 510 B-400 resin can be used for corrosion resistant, reinforced thermosetting plastic equipment including filament wound, hand lay-up and spray-up tanks, pipes, ducts, stacks, scrubbers, linings or other equipment handling corrosive gases, vapors or liquids where a high degree of flame retardancy is required.

General Information
Features	Low viscosity High strength Impact resistance, good Workability, good Good corrosion resistance alkali resistance acid resistance Good toughness Flame retardancy
Uses	Laminate Lining Piping system Water tank
Forms	Liquid
Processing Method	Filament power winding Hand coating

Physical	Nominal Value	Unit	Test Method
Solution Viscosity ¹	425	mPa·s
Gardner Color
Solids Content	57	%

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	35		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3520	MPa	ASTM D638
Tensile Strength	90.0	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.7	%	ASTM D638
Fracture	5.5	%	ASTM D638
Flexural Modulus	3450	MPa	ASTM D790
Flexural Strength	152	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	106	°C	ASTM D648

Additional Information
Properties of cured casting at 25°C.

Note Message
1 .	Brookfield #2 spindle @ 30 rpm

Resin Grade	Manufacturer	Category	Trademark
Megalon® 235ML	Mega Polymers	Nylon 6	Megalon®
FHR EPS 71-7371	Flint Hills Resources, LP	PS (EPS)	FHR EPS
Ecoflex® Supersoft 5	Smooth-On, Inc	Silicone	Ecoflex® Supersoft
Hyundai EP PPF HT340	HYUNDAI EP Co., Ltd.	PP Homopolymer	Hyundai EP PPF
Sylvin 8482-75 Red 6293	Sylvin Technologies Incorporated	PVC+NBR	Sylvin