Hostaform® C 9021 AW XAP² ™ LS
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KU7wPX_Hostaform-C-9021-AW-XAP-LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POM copolymer Injection molding type like C 9021, with special additive modified; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; good wear properties and low coefficient of friction. Reduced emission grade. Emissions according to VDA 275 < 5 mg/kg Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: sliding parts for window lifter. FMVSS = Federal Motor Vehicle Safety Standard (USA) Preliminary Data Sheet |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 1.8 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | ISO 179/1eU |
| 23°C | 130 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 88.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 2.00 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 25.0:1.0 |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 210°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5321 | Spartech Polycom | PP Homopolymer | Spartech |
| TIPPLEN® K 499 | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| Elastocon® 8088BL | Elastocon TPE Technologies | TPE | Elastocon® |
| Edgetek™ NL-20GF/000 BLACK | PolyOne Corporation | Nylon 612 | Edgetek™ |
| Petrothene® LR732013 | LyondellBasell Industries | HDPE | Petrothene® |