LNP™ COLORCOMP™ DX98550H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KRwiue_LNP-COLORCOMP-DX98550H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP DX98550H is an unfilled Polycarbonate resin. Added features of this grade are: Low Extractable, Healthcare. Also known as: LNP* COLORCOMP* Compound PDX-D-98550 LE Product reorder name: DX98550H |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 65.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Elongation 3(Break) | 120 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength | 86.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 MHz) | 0.010 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax EP349U | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| RTP 300 TFE 10 SI 2 | RTP Company | PC | RTP |
| Sarlink® TPV 24955N | Teknor Apex Company | TPE | Sarlink® TPV |
| DENKA POVAL K-24E | Denka Company Limited | PVOH | DENKA POVAL |
| Karina GRAY COLOR CONCENTRATE 18/355-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |