RTP 2899 X 106530 N
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KRcP6Z_RTP-2899-X-106530-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 Overmolding - UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 - 1.8 | % | ASTM D955 |
| Moisture Content | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel strength- Nylon 6 1 | 4.4 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% strain, 3.18mm 2 | 1.17 | MPa | ASTM D412 |
| 100% strain, 3.18mm 3 | 1.59 | MPa | ASTM D412 |
| 300% strain, 3.18mm 4 | 3.03 | MPa | ASTM D412 |
| Tensile Strength 5(Break, 3.20 mm) | 3.45 | MPa | ASTM D412 |
| Tensile Elongation 6(Break) | 500 | % | ASTM D412 |
| Tear Strength 7 | 15.8 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 216 - 249 | °C | |
| Mold Temperature | 48.9 - 65.6 | °C | |
| Injection Pressure | 27.6 - 55.2 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | 90°, 20 in/min, RTP 55, Interface Failure |
| 2 . | C mold, 510mm/min |
| 3 . | Mouth die C, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 500 mm/min |
| 6 . | Mouth die C, 500 mm/min |
| 7 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-961TU | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Moplen HP421H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Yanshan PE 1C7A-1 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Hifax SP 179 | LyondellBasell Industries | PP, Unspecified | Hifax |
| Kynar Flex® 3030-10 | Arkema | PVDF | Kynar Flex® |