Order Products : sales@su-jiao.com
Aurora PVC AP2000 Series 081006
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Aurora Plastics, Inc. |
| Trademark: | Aurora PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KQkvtR_Aurora-PVC-AP2000-Series-081006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A high rate, high impact PVC powder, extrusion compound, for interior application |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 to 1.55 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 22°C) | 77 to 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (22°C) | 2550 | MPa | ASTM D638 |
| Tensile Strength (Yield, 22°C) | 42.1 | MPa | ASTM D638 |
| Flexural Modulus (22°C) | 2410 | MPa | ASTM D790 |
| Flexural Strength (22°C) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (22°C) | 660 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 22°C, Extruded at 380 to 390° F melt temperature 1 | > 80.1 | J/cm | |
| 22°C, Extruded at 380 to 390° F melt temperature 2 | > 178 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.1 | °C | ASTM D648 |
| CLTE - Flow (22°C) | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 3 | HB | ASTM D635 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Procedure B |
| 3 . | No flame spread |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HAIPLEN EP100 CM5 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Hylon® N1000EHL2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LNP™ LUBRICOMP™ RP004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Petro Rabigh PP Y101 | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |
| POCAN® BF 4409 000000 | LANXESS Corporation | PBT | POCAN® |