Ultramid® BG40GM45 HS BK-130
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KQM607_Ultramid-BG40GM45-HS-BK-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
An Ultramid® BG40GM45 HS BK-130 is a pigmented black, heat stabilized, 45 % combined glass and mineral reinforced polyamide 6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimension stability, low warp and resistance to sink-mark formation. Ultramid® BG40GM45 HS BK-130 is ideally suited for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds, interior and exterior doorhandles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Polymer Abbreviation | PA6-(MID+GF)45 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec | ||
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E-185G | Prime Polymer Co., Ltd. | PP Impact Copolymer | Prime Polypro™ |
| Tecoform® PO30 GB20 NL HS | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| Buna® EP G 8850 | LANXESS Corporation | EPDM | Buna® EP |
| ColorRx® PC-1500RX | LTL Color Compounders, Inc. | PC | ColorRx® |
| OmniTech™ PBSN GR30 | OMNI Plastics, LLC | PBT+SAN | OmniTech™ |