LUVOCOM® 1115/XCF/40 Datasheet,PEKK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1115/XCF/40 is a polyetherketone ketone (PEKK) material, which contains a 40% carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1115/XCF/40 are: Flame Retardant Conductivity High stiffness high strength Electrostatic protection LUVOCOM®Typical application fields of 1115/XCF/40 are: engineering/industrial accessories

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 40% filler by weight
Features	Conductivity Rigidity, high High strength Electrostatic discharge protection Good chemical resistance Hydrolysis stability Flame retardancy
Uses	Pump parts Bushing Gear Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.47	g/cm³	ISO 1183
Molding Shrinkage	0.050 - 0.20	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	40000	MPa	ISO 527-2
Tensile Stress (Break)	320	MPa	ISO 527-2
Tensile Strain (Yield)	1.2	%	ISO 527-2
Flexural Modulus	35000	MPa	ISO 178
Flexural Stress	465	MPa	ISO 178
Flexural Strain at Flexural Strength	1.8	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	300	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	55	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	330	°C	ISO 75-2/A
Continuous Use Temperature	260	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	140	°C
Hot air dryer, B	150	°C
Drying Time
Hot air dryer, A	4.0 - 6.0	hr
Hot air dryer, B	4.0 - 8.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	370 - 390	°C
Middle Temperature	380 - 420	°C
Front Temperature	390 - 420	°C
Nozzle Temperature	390 - 420	°C
Processing (Melt) Temp	390	°C
Mold Temperature	180 - 220	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PEKK , Polyetherketoneketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KPDxGU_LUVOCOM-1115-XCF-40.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 4085 TFE 10	RTP Company	PPA	RTP
Quadraflex™ ALE-90A	Biomerics, LLC	TPU-Polyether	Quadraflex™
Unilex™ UP 8034	United Polychem	PP Homopolymer	Unilex™
Flontech® FT-1-TUR-6	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
KRALASTIC® GA-501	Nippon A&L Inc.	ABS	KRALASTIC®