EL-Lene™ M3804RW
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KP6zGD_EL-Lene-M3804RW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M3804RW/RWP is a linear-low density polyethylene with a balance of impact properties, stiffness, and processability. M3804RW/RWP is suitable for rotational molding of storage tanks and general applications. It contains high level of UV stabilizer to give protection for outdoor use. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 20.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 800 | % | ASTM D638 |
| Bending modulus- Transverse flow 3 | 700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact 4(-40°C) | 94.9 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Point | 113 | °C | ASTM D2117 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Melting Temperature | 125 | °C | ASTM D2117 |
| Additional Information |
|---|
| UV Resistance Level, ASTM D2565: 8Oven Temperature: 250 to 300°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 5 mm rotomolded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Utomer UT890 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| Andur 8 APFLM | Anderson Development Company | PUR-Ester/TDI | Andur |
| Kingfa PBT RG30 | Kingfa | PBT | Kingfa PBT |
| Petlon R-Prime M3-G30-00-BK | Petlon Polymers Ltd | PBT+PET | Petlon R-Prime |
| Sumiliteresin® PR-51316 | SBHPP | Phenolic | Sumiliteresin® |